Pb-Co nanowires were electrodeposited in 100 nm nominal pore diameter polycarbonate membranes. Above the T-C of Pb we modelled the behaviour of the wires with a Langevin function, obtaining a Co volume of (1.06 +/- 0.01) x 10(-7) cm(3) divided into clusters of approximate to 10 atoms in size. The magnetic response of the wires in the 3-10 K interval, which comprises T-C, was modelled by adding spherical superconducting Pb grains to the Co clusters; the Pb grains were found to be (87 +/- 6) nm in diameter. The Co clusters were not interacting and were not magnetically screened by the superconducting Pb.
Coexistence of superconductivity and superparamagnetism in Pb-Co electrodeposited nanowires
Riminucci Alberto;
2017
Abstract
Pb-Co nanowires were electrodeposited in 100 nm nominal pore diameter polycarbonate membranes. Above the T-C of Pb we modelled the behaviour of the wires with a Langevin function, obtaining a Co volume of (1.06 +/- 0.01) x 10(-7) cm(3) divided into clusters of approximate to 10 atoms in size. The magnetic response of the wires in the 3-10 K interval, which comprises T-C, was modelled by adding spherical superconducting Pb grains to the Co clusters; the Pb grains were found to be (87 +/- 6) nm in diameter. The Co clusters were not interacting and were not magnetically screened by the superconducting Pb.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.