In this paper, the feasibility of producing Fe(Se,Te)-coated conductors on cost-effective, unbuffered Invar 36 substrates is studied. A suitable substrate with a sharp {001}<100> texture and a misorientation angle lower than 10° was developed, and the possibility of growing epitaxial thin films without any buffer layer was demonstrated. It was also shown that the presence of a Fe(Se,Te) seed layer can improve the in- and out-of-plane orientation of the film. A high-resolution scanning electron microscopy study was performed, and the absence of a superconducting transition has been attributed to Ni poisoning based on X-ray microanalysis. © 2002-2011 IEEE.
Analysis of Fe(Se,Te) films deposited on unbuffered invar 36
Malagoli;Bellingeri;Putti;Ma;Ferdeghini;Braccini;
2019
Abstract
In this paper, the feasibility of producing Fe(Se,Te)-coated conductors on cost-effective, unbuffered Invar 36 substrates is studied. A suitable substrate with a sharp {001}<100> texture and a misorientation angle lower than 10° was developed, and the possibility of growing epitaxial thin films without any buffer layer was demonstrated. It was also shown that the presence of a Fe(Se,Te) seed layer can improve the in- and out-of-plane orientation of the film. A high-resolution scanning electron microscopy study was performed, and the absence of a superconducting transition has been attributed to Ni poisoning based on X-ray microanalysis. © 2002-2011 IEEE.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.