An immobilized photoactive TiO coating grown directly on titanium meshes was successfully exploited for the electrochemical photocatalytic degradation of carbamazepine in real secondary wastewater effluent. The catalyst was prepared by Plasma Electrolytic Oxidation and during the photocatalytic water treatment an electrical polarization (bias) was applied to the catalyst. The investigated process was compared with the conventional one employing suspended TiO powder (Degussa P25). Results showed that carbamazepine degradation rate follows the order UV/supported TiO+bias ? UV/TiO Degussa P25 > UV/supported TiO > UV. The investigation also included the identification of other micropollutants and degradation products. This allowed the detection of 201 compounds present in the secondary wastewater effluent employed for the photocatalysis tests, 51 of them also successfully associated to compounds of emerging concern (CECs), and 194 to transformation products (TPs). The degradation of detected compounds followed first-order kinetics and the mean kinetic constant values of the 51 CECs resulted to be 0.048, 0.035 and 0.043 min for the TiO+Bias + UV, TiO+UV and UV, respectively. As for TPs, results showed that the TiO+Bias + UV treatment is much more efficient than both TiO+UV and UV in minimizing the intensity of the organics in the real wastewater. Such a better performance was more pronounced at higher reaction time reaching 60% reduction of mean peak area of TPs at 90 min of reaction. Among the detected TPs also compounds belonging to known carbamazepine TPs were found. This allowed to propose a degradation pathway of carbamazepine. The supported catalyst was positively tested for 15 cycles demonstrating that it has the potential to be used in real wastewater tertiary steps aimed at removing CECs.
Degradation of emerging organic pollutants in wastewater effluents by electrochemical photocatalysis on nanostructured TiO2 meshes
Murgolo S;Mascolo G
2019
Abstract
An immobilized photoactive TiO coating grown directly on titanium meshes was successfully exploited for the electrochemical photocatalytic degradation of carbamazepine in real secondary wastewater effluent. The catalyst was prepared by Plasma Electrolytic Oxidation and during the photocatalytic water treatment an electrical polarization (bias) was applied to the catalyst. The investigated process was compared with the conventional one employing suspended TiO powder (Degussa P25). Results showed that carbamazepine degradation rate follows the order UV/supported TiO+bias ? UV/TiO Degussa P25 > UV/supported TiO > UV. The investigation also included the identification of other micropollutants and degradation products. This allowed the detection of 201 compounds present in the secondary wastewater effluent employed for the photocatalysis tests, 51 of them also successfully associated to compounds of emerging concern (CECs), and 194 to transformation products (TPs). The degradation of detected compounds followed first-order kinetics and the mean kinetic constant values of the 51 CECs resulted to be 0.048, 0.035 and 0.043 min for the TiO+Bias + UV, TiO+UV and UV, respectively. As for TPs, results showed that the TiO+Bias + UV treatment is much more efficient than both TiO+UV and UV in minimizing the intensity of the organics in the real wastewater. Such a better performance was more pronounced at higher reaction time reaching 60% reduction of mean peak area of TPs at 90 min of reaction. Among the detected TPs also compounds belonging to known carbamazepine TPs were found. This allowed to propose a degradation pathway of carbamazepine. The supported catalyst was positively tested for 15 cycles demonstrating that it has the potential to be used in real wastewater tertiary steps aimed at removing CECs.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.