The combination of core/shell geometry and band gap engineering in nanowire heterostructures can be employed to realize systems with novel transport and optical properties. Here, we report on the growth of InAs/InP/GaAsSb core-dual-shell nanowires by catalyst-free chemical beam epitaxy on Si(111) substrates. Detailed morphological, structural, and compositional analyses of the nanowires as a function of growth parameters were carried out by scanning and transmission electron microscopy and by energy-dispersive X-ray spectroscopy. Furthermore, by combining the scanning transmission electron microscopy-Moiré technique with geometric phase analysis, we studied the residual strain and the relaxation mechanisms in this system. We found that InP shell facets are well-developed along all the crystallographic directions only when the nominal thickness is above 1 nm, suggesting an island-growth mode. Moreover, the crystallographic analysis indicates that both InP and GaAsSb shells grow almost coherently to the InAs core along the «112»direction and elastically compressed along the «110»direction. For InP shell thickness above 8 nm, some dislocations and roughening occur at the interfaces. This study provides useful general guidelines for the fabrication of high-quality devices based on these core-dual-shell nanowires.
Growth and Strain Relaxation Mechanisms of InAs/InP/GaAsSb Core-Dual-Shell Nanowires
Arif O;Zannier V
;Rossi F;Ercolani D;Beltram F;Sorba L
2020
Abstract
The combination of core/shell geometry and band gap engineering in nanowire heterostructures can be employed to realize systems with novel transport and optical properties. Here, we report on the growth of InAs/InP/GaAsSb core-dual-shell nanowires by catalyst-free chemical beam epitaxy on Si(111) substrates. Detailed morphological, structural, and compositional analyses of the nanowires as a function of growth parameters were carried out by scanning and transmission electron microscopy and by energy-dispersive X-ray spectroscopy. Furthermore, by combining the scanning transmission electron microscopy-Moiré technique with geometric phase analysis, we studied the residual strain and the relaxation mechanisms in this system. We found that InP shell facets are well-developed along all the crystallographic directions only when the nominal thickness is above 1 nm, suggesting an island-growth mode. Moreover, the crystallographic analysis indicates that both InP and GaAsSb shells grow almost coherently to the InAs core along the «112»direction and elastically compressed along the «110»direction. For InP shell thickness above 8 nm, some dislocations and roughening occur at the interfaces. This study provides useful general guidelines for the fabrication of high-quality devices based on these core-dual-shell nanowires.File | Dimensione | Formato | |
---|---|---|---|
prod_418617-doc_149205.pdf
solo utenti autorizzati
Descrizione: Growth and Strain Relaxation Mechanisms of InAs/InP/GaAsSb Core-Dual-Shell Nanowires
Tipologia:
Versione Editoriale (PDF)
Licenza:
NON PUBBLICO - Accesso privato/ristretto
Dimensione
8.66 MB
Formato
Adobe PDF
|
8.66 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.