Single walled carbon nanotube/n-Si (SWCNT/n-Si) hetero-junctions have been obtained by depositing SWCNT ultra-thin films on the surface of an n-Si substrate by dry transfer method. The as obtained junctions are photo sensitive in the measured wavelength range (300-1000 nm) and show zero bias responsivity and detectivity values of the order of 1 A W-1 and 1014 Jones respectively, which are higher than those previously observed in carbon based devices. Moreover, under on-off light excitation, the junctions show response speed as fast as 1 ?s or better and noise equivalent powers comparable to commercial Si photomultipliers. Current-voltage measurements in dark and under illumination suggest that the devices consist of Schottky and semiconductor/semiconductor junctions both contributing to the fast and high responses observed.
Single walled carbon nanotube/Si heterojunctions for high responsivity photodetectors
Scagliotti M;
2017
Abstract
Single walled carbon nanotube/n-Si (SWCNT/n-Si) hetero-junctions have been obtained by depositing SWCNT ultra-thin films on the surface of an n-Si substrate by dry transfer method. The as obtained junctions are photo sensitive in the measured wavelength range (300-1000 nm) and show zero bias responsivity and detectivity values of the order of 1 A W-1 and 1014 Jones respectively, which are higher than those previously observed in carbon based devices. Moreover, under on-off light excitation, the junctions show response speed as fast as 1 ?s or better and noise equivalent powers comparable to commercial Si photomultipliers. Current-voltage measurements in dark and under illumination suggest that the devices consist of Schottky and semiconductor/semiconductor junctions both contributing to the fast and high responses observed.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.