Co-N-C and Fe-N-C electrocatalysts have been prepared by mixing Fe or Co precursors, ethylene diamine tetra acetic acid (EDTA) as a nitrogen source, and an oxidized carbon. These materials were thermally treated at 800 C or 1000 C under nitrogen flow to produce four samples, named CoNC8, CoNC10, FeNC8, and FeNC10. They have been physicochemically characterized by X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Direct methanol fuel cell (DMFC) analyses have been carried out to investigate the performance of the nonprecious cathode catalysts, using a low amount of Pt (0.7 mg/cm2) at the anode side. It appears that FeNC8 is the best performing low-cost cathode catalyst in terms of higher oxygen reduction reaction activity and methanol tolerance.
Application of Low-Cost Me-N-C (Me = Fe or Co) Electrocatalysts Derived from EDTA in Direct Methanol Fuel Cells (DMFCs)
Carmelo Lo Vecchio;Vincenzo Baglio
2018
Abstract
Co-N-C and Fe-N-C electrocatalysts have been prepared by mixing Fe or Co precursors, ethylene diamine tetra acetic acid (EDTA) as a nitrogen source, and an oxidized carbon. These materials were thermally treated at 800 C or 1000 C under nitrogen flow to produce four samples, named CoNC8, CoNC10, FeNC8, and FeNC10. They have been physicochemically characterized by X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Direct methanol fuel cell (DMFC) analyses have been carried out to investigate the performance of the nonprecious cathode catalysts, using a low amount of Pt (0.7 mg/cm2) at the anode side. It appears that FeNC8 is the best performing low-cost cathode catalyst in terms of higher oxygen reduction reaction activity and methanol tolerance.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.