Bi films deposited on InAs(111) A and B sides have been studied by photoemission electron microscopy. A series of snapshots acquired during sequential annealing of the interfaces at temperatures below and above the melting temperature of Bi allowed obtaining a comprehensive image of the topographic and chemical evolutions of the Bi films that are found to be InAs side dependent. On the A side, a morphology of circular patterns controlled by Bi atoms mobility is observed. The patterns are formed on the pristine In-terminated InAs(111) surface covered by a weakly bonded Bi bilayer. On the B side, no particular morphology is observed due to a stronger chemical interaction between Bi and As atoms as evidenced by the spatially-resolved core-level photoelectron spectra. (C) 2016 Elsevier B.V. All rights reserved.
Bi atoms mobility-driven circular domains at the Bi/InAs(111) interface
Vobornik I;Fujii J;
2016
Abstract
Bi films deposited on InAs(111) A and B sides have been studied by photoemission electron microscopy. A series of snapshots acquired during sequential annealing of the interfaces at temperatures below and above the melting temperature of Bi allowed obtaining a comprehensive image of the topographic and chemical evolutions of the Bi films that are found to be InAs side dependent. On the A side, a morphology of circular patterns controlled by Bi atoms mobility is observed. The patterns are formed on the pristine In-terminated InAs(111) surface covered by a weakly bonded Bi bilayer. On the B side, no particular morphology is observed due to a stronger chemical interaction between Bi and As atoms as evidenced by the spatially-resolved core-level photoelectron spectra. (C) 2016 Elsevier B.V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.