Surfactant-coated ytterbium nanoparticles were produced by Nd:YAG laser ablation of a Yb bulk target immersed in sodium bis(2-ethylhexyl)sulfosuccinate (AOT)/n-heptane micellar solution. In our experimental conditions, as highlighted by IR spectroscopy, AOT molecules are not decomposed by the intense laser pulses but play a pivotal role in the stabilisation of Yb nanoparticles. The formation of Yb nanoparticles in the liquid phase was monitored by UVVis spectroscopy whereas the Yb/AOT composites obtained by evaporation of the organic solvent were characterised by XPS and TEM. Data analysis consistently shows the presence of surfactant-coated, nearly spherical and non-interacting Yb nanoparticles of mean diameter of 3 nm. Moreover, the presence of bigger polycrystalline nanoparticles (about 30%) in coexistence with smaller mono crystalline ones indicates that, after the rapid formation of the pristine Yb nanoparticles from plume condensation, two processes effectively compete for their size distribution: nanoparticle agglomeration and surfactant adsorption.
Synthesis of Yb nanoparticles by laser ablation of Yb target in AOT reverse micellar solution
Calandra P;Lombardo D;Trusso S;
2010
Abstract
Surfactant-coated ytterbium nanoparticles were produced by Nd:YAG laser ablation of a Yb bulk target immersed in sodium bis(2-ethylhexyl)sulfosuccinate (AOT)/n-heptane micellar solution. In our experimental conditions, as highlighted by IR spectroscopy, AOT molecules are not decomposed by the intense laser pulses but play a pivotal role in the stabilisation of Yb nanoparticles. The formation of Yb nanoparticles in the liquid phase was monitored by UVVis spectroscopy whereas the Yb/AOT composites obtained by evaporation of the organic solvent were characterised by XPS and TEM. Data analysis consistently shows the presence of surfactant-coated, nearly spherical and non-interacting Yb nanoparticles of mean diameter of 3 nm. Moreover, the presence of bigger polycrystalline nanoparticles (about 30%) in coexistence with smaller mono crystalline ones indicates that, after the rapid formation of the pristine Yb nanoparticles from plume condensation, two processes effectively compete for their size distribution: nanoparticle agglomeration and surfactant adsorption.File | Dimensione | Formato | |
---|---|---|---|
prod_40392-doc_18671.pdf
non disponibili
Descrizione: articolo pubblicato
Dimensione
687.11 kB
Formato
Adobe PDF
|
687.11 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.