The present paper reports about the experimental characterization of a recently developed composite sorbent of water, LiCl/vermiculite, for thermal energy storage applications. The sorption ability as well as the thermal storage capacity (TSC) of the material itself were tested in a dedicated TG/DSC apparatus, under two relevant boundary conditions, namely, seasonal (SS) and daily (DS) storage applications. The dynamic behavior of the composite sorbent was tested by means of a G-LTJ apparatus in flat-plate adsorber configuration, under both SS and DS working conditions. Finally, preliminary tests on a lab-scale TES configuration were performed and reported. The main outcomes confirm that the composite is promising for TES applications, reaching the TSC up to 2.15 kJ/g under SS conditions. The stability of the composite was proven for 14 consecutive sorption/desorption cycles under conditions similar to those at real SS and DS cycles. The kinetic adsorption tests confirmed a slowdown of the sorption dynamics when passing from 1.7-2.0 mm to 2.36-2.80 mm of the grain size. Furthermore, the adsorption kinetic under SS mode is faster than of DS one. The preliminary testing in the lab-scale TES at SS cycle allowed getting TSC up to 1.25 kJ/g with a specific power up to 2.1 kW/kg.
Experimental characterization of the LiCl/vermiculite composite for sorption heat storage applications|Caractérisation expérimentale du composite LiCl/vermiculite pour les applications de stockage de chaleur par sorption
Brancato V;Sapienza A;Palomba V;Vasta S;Frazzica A;
2019
Abstract
The present paper reports about the experimental characterization of a recently developed composite sorbent of water, LiCl/vermiculite, for thermal energy storage applications. The sorption ability as well as the thermal storage capacity (TSC) of the material itself were tested in a dedicated TG/DSC apparatus, under two relevant boundary conditions, namely, seasonal (SS) and daily (DS) storage applications. The dynamic behavior of the composite sorbent was tested by means of a G-LTJ apparatus in flat-plate adsorber configuration, under both SS and DS working conditions. Finally, preliminary tests on a lab-scale TES configuration were performed and reported. The main outcomes confirm that the composite is promising for TES applications, reaching the TSC up to 2.15 kJ/g under SS conditions. The stability of the composite was proven for 14 consecutive sorption/desorption cycles under conditions similar to those at real SS and DS cycles. The kinetic adsorption tests confirmed a slowdown of the sorption dynamics when passing from 1.7-2.0 mm to 2.36-2.80 mm of the grain size. Furthermore, the adsorption kinetic under SS mode is faster than of DS one. The preliminary testing in the lab-scale TES at SS cycle allowed getting TSC up to 1.25 kJ/g with a specific power up to 2.1 kW/kg.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.