Colloidal aqueous dispersions of nanometric NiAl, ZnAl, NiCr, ZnCr, NiFe, and MgFe hydrotalcite-like compounds were prepared in a water/cetyltrimethylammonium bromide/n-butanol/isooctane microemulsion. Particle sizes were analyzed with different techniques, and the results confirm dimensions between 10 and 30 nm, except for ZnAl-HTlc (150-200 nm). A good colloidal stability of HTlc-NPs aqueous dispersions, investigated with DLS and Pz measurements, was obtained without the need for any stabilizing agent. SEM images clearly showed that the obtained HTlc posses a high tendency to spontaneously form homogeneous and dense stacking of plate-like HTlc crystals directly from aqueous solution, giving rise to the developing of functional materials in optical, electrical and magnetic fields. (C) 2012 Elsevier Inc. All rights reserved.
Synthesis of colloidal dispersions of NiAl, ZnAl, NiCr, ZnCr, NiFe, and MgFe hydrotalcite-like nanoparticles
Posati Tamara;
2012
Abstract
Colloidal aqueous dispersions of nanometric NiAl, ZnAl, NiCr, ZnCr, NiFe, and MgFe hydrotalcite-like compounds were prepared in a water/cetyltrimethylammonium bromide/n-butanol/isooctane microemulsion. Particle sizes were analyzed with different techniques, and the results confirm dimensions between 10 and 30 nm, except for ZnAl-HTlc (150-200 nm). A good colloidal stability of HTlc-NPs aqueous dispersions, investigated with DLS and Pz measurements, was obtained without the need for any stabilizing agent. SEM images clearly showed that the obtained HTlc posses a high tendency to spontaneously form homogeneous and dense stacking of plate-like HTlc crystals directly from aqueous solution, giving rise to the developing of functional materials in optical, electrical and magnetic fields. (C) 2012 Elsevier Inc. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.