Layered semimetallic 1T-TiTe2 has been reported to exhibit pressure-induced superconductivity, and some nontrivial topological states have also been suggested to appear under pressure. Here we investigate the optical properties of this compound by infrared reflectance measurements over a broad energy range under quasihydrostatic pressures up to 22 GPa. The observed conspicuous changes of infrared phonon spectra, in combination with x-ray diffraction data, provide clear evidence of an irreversible structural transition into a noncentrosymmetric space group (P3m1->P3m1) at a low pressure (~2.3 GPa), before undergoing a subsequent transition to a monoclinic phase (C2/m) above 12 GPa. The pressure-induced irreversible gain of the low-frequency spectral weight of optical conductivity further supports the above crystal structure modification. The irreversible structural modification and associated change in electronic structure have been argued to be responsible for the emergence of superconductivity with enhanced Tc and its persistence upon decompression. The low-pressure structural instability in 1T-TiTe2 makes it necessary to revisit the theoretical investigation of its topological nature.
Infrared spectroscopic measurements of structural transition and charge dynamics in 1 T-TiTe2 under pressure
Piccirilli F;Lupi S;
2019
Abstract
Layered semimetallic 1T-TiTe2 has been reported to exhibit pressure-induced superconductivity, and some nontrivial topological states have also been suggested to appear under pressure. Here we investigate the optical properties of this compound by infrared reflectance measurements over a broad energy range under quasihydrostatic pressures up to 22 GPa. The observed conspicuous changes of infrared phonon spectra, in combination with x-ray diffraction data, provide clear evidence of an irreversible structural transition into a noncentrosymmetric space group (P3m1->P3m1) at a low pressure (~2.3 GPa), before undergoing a subsequent transition to a monoclinic phase (C2/m) above 12 GPa. The pressure-induced irreversible gain of the low-frequency spectral weight of optical conductivity further supports the above crystal structure modification. The irreversible structural modification and associated change in electronic structure have been argued to be responsible for the emergence of superconductivity with enhanced Tc and its persistence upon decompression. The low-pressure structural instability in 1T-TiTe2 makes it necessary to revisit the theoretical investigation of its topological nature.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.