Measurements of electrical conductivity were carried out at temperatures ranging between 77 K and 450 K on high vacuum thermal reduced graphene oxide (rGO) films. The investigated samples were characterized in composition and structure before being analyzed in terms of electrical conduction. Their electrical conductivity was also measured in air at room temperature. Measurements have demonstrated that at first graphene oxide (GO) was not stable both in air and vacuum. It stabilized after having been subjected to 7 thermal cycles under high vacuum conditions, about 10 torr, up to a T of 450 K. At room temperature the initial GO material had a very low conductivity, of the order of 10? x cm, which increased to about 2.5 ?x cm when it was thermal stabilized in rGO. The stabilization process, induced by the high vacuum heating procedure, seems due to a good reduction of GO, which gives rise to such expansion of the conjugated ?-electron system that a band-like transport with small thermal activation energies (E = 10-50 meV) occurs. The performed electrical conductivity measurements are presented and discussed.

Band-like transport in high vacuum thermal reduced graphene oxide films

Salvato G;Di Marco G;Fazio B;
2019

Abstract

Measurements of electrical conductivity were carried out at temperatures ranging between 77 K and 450 K on high vacuum thermal reduced graphene oxide (rGO) films. The investigated samples were characterized in composition and structure before being analyzed in terms of electrical conduction. Their electrical conductivity was also measured in air at room temperature. Measurements have demonstrated that at first graphene oxide (GO) was not stable both in air and vacuum. It stabilized after having been subjected to 7 thermal cycles under high vacuum conditions, about 10 torr, up to a T of 450 K. At room temperature the initial GO material had a very low conductivity, of the order of 10? x cm, which increased to about 2.5 ?x cm when it was thermal stabilized in rGO. The stabilization process, induced by the high vacuum heating procedure, seems due to a good reduction of GO, which gives rise to such expansion of the conjugated ?-electron system that a band-like transport with small thermal activation energies (E = 10-50 meV) occurs. The performed electrical conductivity measurements are presented and discussed.
2019
Istituto per i Processi Chimico-Fisici - IPCF
Graphene oxide
Reduced graphene oxide
Electrical conductivity
I-V characteristics
File in questo prodotto:
File Dimensione Formato  
prod_425208-doc_172835.pdf

solo utenti autorizzati

Descrizione: PDF
Tipologia: Versione Editoriale (PDF)
Dimensione 1.73 MB
Formato Adobe PDF
1.73 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.14243/406456
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 31
  • ???jsp.display-item.citation.isi??? 31
social impact