A Spark Plasma Sintering (SPS) furnace was used to Flash-Sinter (FS) pure titanium diboride (TiB2) powder. A pre-sintering green body (Ø= 20 mm, relative density ?60%) was used for the Flash-SPS using a dieless configuration with current passing entirely across the sample. The results show that the samples were densified in very short time (< 60 seconds) up to 87% of theoretical density. TiB2 obtained by Flash-SPS was characterized using XRD and SEM analysis.
Flash spark plasma sintering of pure TiB2
Simone Failla;Diletta Sciti
2020
Abstract
A Spark Plasma Sintering (SPS) furnace was used to Flash-Sinter (FS) pure titanium diboride (TiB2) powder. A pre-sintering green body (Ø= 20 mm, relative density ?60%) was used for the Flash-SPS using a dieless configuration with current passing entirely across the sample. The results show that the samples were densified in very short time (< 60 seconds) up to 87% of theoretical density. TiB2 obtained by Flash-SPS was characterized using XRD and SEM analysis.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.