The galvanic displacement reaction between sacrificial PbO2 layers and Fe(II) ions has been carried out in mildly acid acetate solutions. The effect of experimental variables, like morphology of the PbO2 layers, solution pH, temperature and concentration of Fe(II) ions, has been investigated by combining electrochemical methods, SEM-EDS, XRD and XPS. The reaction between PbO2 and Fe(II) ions produced secondary dual layers, consisting of an inner amorphous FeOOH film and an outer crystalline ?-FeOOH deposit, respectively. This peculiar behavior was in contrast with analogous reactions involving other transition metal ions, which yielded only continuous amorphous secondary oxide layers. PbO2/FeOOH layers were tested as anodes for the oxygen evolution reaction in basic media.
Deposition of FeOOH layers onto porous PbO2 by galvanic displacement and their use as electrocatalysts for oxygen evolution reaction
Comisso N;Armelao L;Cattarin S;Fasolin S;Mattarozzi L;Musiani M;Rancan M;Verlato E
2021
Abstract
The galvanic displacement reaction between sacrificial PbO2 layers and Fe(II) ions has been carried out in mildly acid acetate solutions. The effect of experimental variables, like morphology of the PbO2 layers, solution pH, temperature and concentration of Fe(II) ions, has been investigated by combining electrochemical methods, SEM-EDS, XRD and XPS. The reaction between PbO2 and Fe(II) ions produced secondary dual layers, consisting of an inner amorphous FeOOH film and an outer crystalline ?-FeOOH deposit, respectively. This peculiar behavior was in contrast with analogous reactions involving other transition metal ions, which yielded only continuous amorphous secondary oxide layers. PbO2/FeOOH layers were tested as anodes for the oxygen evolution reaction in basic media.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.