Measuring TiO2N and AgHEC Airborne Particle Density during a Spray Coating Process

Effective particle density is a key parameter for assessing inhalation exposure of engineeredNPs in occupational environments. In this paper, particle density measurements were carried out using two different techniques: one based on the ratio between mass and volumetric particle concentrations; the other one based on the ratio between aerodynamic and geometric particle diameter. These different approaches were applied to both field- and laboratory-scale atomization processes where the two target NPs (N-doped TiO2, TiO2N and AgNPs capped with a quaternized hydroxyethylcellulose, AgHEC) were generated. Spray tests using TiO2N were observed to release more and bigger particles than tests with AgHEC, as indicated by the measured particle mass concentrations and volumes. Our findings give an effective density of TiO2N particle to be in a similar range betweenfield and laboratory measurements (1.8 ± 0.5 g/cm3 ); while AgHEC particle density showed wide variations (3.0 ± 0.5 g/cm3 and 1.2 + 0.1 g/cm3 for field and laboratory campaigns, respectively). This finding leads to speculation regarding the composition of particles emitted because atomized particle fragments may contain different Ag-to-HEC ratios, leading to different density values. A further uncertainty factor is probably related to low process emissions, making the subtraction of background concentrations from AgHEC process emissions unreliable.