We present an innovative approach to integrate arrays of isolated, strain-free GaN crystals on patterned Si substrates. First, micrometer-sized pillars are patterned onto Si(0 0 1) substrates. Subsequently, 2.5 ?m Si substrates are deposited by low-energy plasma-enhanced chemical vapor deposition, forming crystals mostly bounded by {1 1 1}, {1 1 3}, and {15 3 23} facets. Plasma-assisted molecular beam epitaxy is then used for GaN deposition. GaN crystals with slanted {0 0 0 1} facets having a root-mean-square surface roughness of 0.7 nm are obtained for a deposited material thickness of >3 ?m. Microphotoluminescence measurements performed at room and cryogenic temperature show no yellow luminescence and a neutral donor-bound A exciton transition at 3.471 eV (10 K) with a full width at half-maximum of 10 meV. Microphotoluminescence and micro-Raman spectra reveal that GaN grown on Si pillars is strain-free. Our results indicate that the shape of GaN crystals can be tuned by the pattern periodicity and that a reduction of threading dislocations is achieved in their top part.
Integration of GaN Crystals on Micropatterned Si(001) Substrates by Plasma-Assisted Molecular Beam Epitaxy
Calarco R;
2015
Abstract
We present an innovative approach to integrate arrays of isolated, strain-free GaN crystals on patterned Si substrates. First, micrometer-sized pillars are patterned onto Si(0 0 1) substrates. Subsequently, 2.5 ?m Si substrates are deposited by low-energy plasma-enhanced chemical vapor deposition, forming crystals mostly bounded by {1 1 1}, {1 1 3}, and {15 3 23} facets. Plasma-assisted molecular beam epitaxy is then used for GaN deposition. GaN crystals with slanted {0 0 0 1} facets having a root-mean-square surface roughness of 0.7 nm are obtained for a deposited material thickness of >3 ?m. Microphotoluminescence measurements performed at room and cryogenic temperature show no yellow luminescence and a neutral donor-bound A exciton transition at 3.471 eV (10 K) with a full width at half-maximum of 10 meV. Microphotoluminescence and micro-Raman spectra reveal that GaN grown on Si pillars is strain-free. Our results indicate that the shape of GaN crystals can be tuned by the pattern periodicity and that a reduction of threading dislocations is achieved in their top part.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.