The effect of MgF2 as a sintering additive for the preparation of YAG ceramics via spark plasma sintering (SPS) is investigated with promising results, as nearly complete densification (0.58% porosity) is achieved at relatively low temperature and moderate pressure. Higher temperature and dwell time resulted in a translucent/trans-parent body. On the other side, significant grain growth was observed with MgF2 addition.
Magnesium fluoride (MgF2) - A novel sintering additive for the preparation of transparent YAG ceramics via SPS
Hostasa JanSecondo
;
2022
Abstract
The effect of MgF2 as a sintering additive for the preparation of YAG ceramics via spark plasma sintering (SPS) is investigated with promising results, as nearly complete densification (0.58% porosity) is achieved at relatively low temperature and moderate pressure. Higher temperature and dwell time resulted in a translucent/trans-parent body. On the other side, significant grain growth was observed with MgF2 addition.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
Necina 2021 post-print DOI.pdf
Open Access dal 05/02/2024
Tipologia:
Documento in Post-print
Licenza:
Creative commons
Dimensione
1.5 MB
Formato
Adobe PDF
|
1.5 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.