A two-part discussion of the B-Hf-Ni system by CALPHAD and Experimental methods is presented which shows how efficient application of the results can lead to a greater understanding of the behavior as well as insight into the direction of future research. This Part 1 is devoted to the calculation of the ternary sections of the B-Hf-Ni phase diagram at various temperatures, which are of special interest for the experimental work presented in Part 2, together with the evaluation of specific isopleths, to support the interpretation of solidification phenomena of the alloys used in the experimental part and of the resulting room temperature structures. '
Wettability of HfB2 by molten Ni(B) alloys interpreted by CALPHAD methods. Part 1: definition of the B-Hf-Ni System
M L Muolo;F Valenza;A Passerone
2010
Abstract
A two-part discussion of the B-Hf-Ni system by CALPHAD and Experimental methods is presented which shows how efficient application of the results can lead to a greater understanding of the behavior as well as insight into the direction of future research. This Part 1 is devoted to the calculation of the ternary sections of the B-Hf-Ni phase diagram at various temperatures, which are of special interest for the experimental work presented in Part 2, together with the evaluation of specific isopleths, to support the interpretation of solidification phenomena of the alloys used in the experimental part and of the resulting room temperature structures. '| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_22411-doc_3886.pdf
non disponibili
Descrizione: Wettability of HfB2 by molten Ni(B) alloys interpreted by CALPHAD methods. Part 1: Definition of the B-Hf-Ni system
Dimensione
662.55 kB
Formato
Adobe PDF
|
662.55 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.