The properties of graphene oxide foils were modified by excimer laser irradiation at different fluences and times. The irradiations were performed in air and in vacuum using a pulsed UV laser operating at 248-nm wavelength and 23-ns pulse duration. Measurements of ablation yield, microscope surface morphology and Raman spectroscopy were performed. The residual surface shows a significant oxygen reduction due to the removing of functional oxygen groups, a thickness reduction due to the removal of graphene layers depending on the used laser shots and a presence of defects in the graphene sheets as evident by the Raman spectroscopy investigation.
Graphene oxide modifications induced by excimer laser irradiations
Velardi Luciano;
2022
Abstract
The properties of graphene oxide foils were modified by excimer laser irradiation at different fluences and times. The irradiations were performed in air and in vacuum using a pulsed UV laser operating at 248-nm wavelength and 23-ns pulse duration. Measurements of ablation yield, microscope surface morphology and Raman spectroscopy were performed. The residual surface shows a significant oxygen reduction due to the removing of functional oxygen groups, a thickness reduction due to the removal of graphene layers depending on the used laser shots and a presence of defects in the graphene sheets as evident by the Raman spectroscopy investigation.| File | Dimensione | Formato | |
|---|---|---|---|
|
Surface Interface Analysis - 2022.pdf
accesso aperto
Descrizione: pdf del paper
Tipologia:
Versione Editoriale (PDF)
Licenza:
Creative commons
Dimensione
2.23 MB
Formato
Adobe PDF
|
2.23 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.