Van der Waals ?-MoO samples offer a wide range of attractive catalytic, electronic, and optical properties. We present herein an emission Mössbauer spectroscopy (eMS) study of the electric-field gradient (EFG) anisotropy in crystalline free-standing ?-MoO samples. Although ?-MoO is a two-dimensional (2D) material, scanning electron microscopy shows that the crystals are 0.5-5-µm thick. The combination of X-ray diffraction and micro-Raman spectroscopy, performed after sample preparation, provided evidence of the phase purity and crystal quality of the samples. The eMS measurements were conducted following the implantation of Mn (t = 1.5 min), which decays to the Fe, 14.4 keV Mössbauer state. The eMS spectra of the samples are dominated by a paramagnetic doublet (D1) with an angular dependence, pointing to the Fe probe ions being in a crystalline environment. It is attributed to an asymmetric EFG at the eMS probe site originating from strong in-plane covalent bonds and weak out-of-plane van der Waals interactions in the 2D material. Moreover, a second broad component, D2, can be assigned to Fe defects that are dynamically generated during the online measurements. The results are compared to ab initio simulations and are discussed in terms of the in-plane and out-of-plane interactions in the system.
Anisotropy of the Electric Field Gradient in Two-Dimensional ?-MoO3 Investigated by57 Mn(57 Fe) Emission Mössbauer Spectroscopy
Mantovan Roberto;
2022
Abstract
Van der Waals ?-MoO samples offer a wide range of attractive catalytic, electronic, and optical properties. We present herein an emission Mössbauer spectroscopy (eMS) study of the electric-field gradient (EFG) anisotropy in crystalline free-standing ?-MoO samples. Although ?-MoO is a two-dimensional (2D) material, scanning electron microscopy shows that the crystals are 0.5-5-µm thick. The combination of X-ray diffraction and micro-Raman spectroscopy, performed after sample preparation, provided evidence of the phase purity and crystal quality of the samples. The eMS measurements were conducted following the implantation of Mn (t = 1.5 min), which decays to the Fe, 14.4 keV Mössbauer state. The eMS spectra of the samples are dominated by a paramagnetic doublet (D1) with an angular dependence, pointing to the Fe probe ions being in a crystalline environment. It is attributed to an asymmetric EFG at the eMS probe site originating from strong in-plane covalent bonds and weak out-of-plane van der Waals interactions in the 2D material. Moreover, a second broad component, D2, can be assigned to Fe defects that are dynamically generated during the online measurements. The results are compared to ab initio simulations and are discussed in terms of the in-plane and out-of-plane interactions in the system.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.