The effect of the presence of poly(vinyl pyrrolidone) (PVP) on the copper nanoparticle formation, obtained by UV irradiation of ethanol solution of Cu(acac)(2) (acac = 2,4-pentanedionato), was investigated. At 254 nm, in conditions of light completely absorbed by complex, the PVP exhibited protective and stabilizing effects, as shown by the formation of a colloidal copper solution and by a block of the heterogeneous process, which leads to thin film formation on the quartz walls. The colloidal solution was tested for several months by plasmon position and it was found that it remained unaltered in inert atmosphere, but returned to the starting complex on contact with air. The PVP ability to control the particle size was investigated by carrying out photoreduction sensitized by Hacac at 254 and 300 nm, in the presence of PVP concentration varying from 0 to 0.2 M. In this range it was possible to obtain copper nanoparticles of dimensions decreasing from 30 to 4 nm. Besides this, the PVP (0.005-0.05 M) role as sensitizer was investigated by irradiating solutions of Cu(acac)(2) at 300 nm which is an inactive wavelength for copper reduction by direct light absorption. It was found that the PVP was an efficient sensitizer of the copper photoreduction. The nanoparticles were characterized by plasmon band, Trasmission Electron Microscope (TEM) as well as Dynamic Light Scattering (DSL) analysis. The overall results evidence the advantages of the PVP use in the nanoparticle copper formation through the photochemical technique such as the exclusive formation of colloidal copper, their size control, stable colloidal solution and complete return to the starting complex.
Photochemical synthesis of copper nanoparticles incorporated in poly(vinyl pyrrolidone)
Bongiorno C
2008
Abstract
The effect of the presence of poly(vinyl pyrrolidone) (PVP) on the copper nanoparticle formation, obtained by UV irradiation of ethanol solution of Cu(acac)(2) (acac = 2,4-pentanedionato), was investigated. At 254 nm, in conditions of light completely absorbed by complex, the PVP exhibited protective and stabilizing effects, as shown by the formation of a colloidal copper solution and by a block of the heterogeneous process, which leads to thin film formation on the quartz walls. The colloidal solution was tested for several months by plasmon position and it was found that it remained unaltered in inert atmosphere, but returned to the starting complex on contact with air. The PVP ability to control the particle size was investigated by carrying out photoreduction sensitized by Hacac at 254 and 300 nm, in the presence of PVP concentration varying from 0 to 0.2 M. In this range it was possible to obtain copper nanoparticles of dimensions decreasing from 30 to 4 nm. Besides this, the PVP (0.005-0.05 M) role as sensitizer was investigated by irradiating solutions of Cu(acac)(2) at 300 nm which is an inactive wavelength for copper reduction by direct light absorption. It was found that the PVP was an efficient sensitizer of the copper photoreduction. The nanoparticles were characterized by plasmon band, Trasmission Electron Microscope (TEM) as well as Dynamic Light Scattering (DSL) analysis. The overall results evidence the advantages of the PVP use in the nanoparticle copper formation through the photochemical technique such as the exclusive formation of colloidal copper, their size control, stable colloidal solution and complete return to the starting complex.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.