Dry reforming of methane with ratio CH4/CO2 = 1 is studied using supported Ni catalysts on SBA-15 modified by CeMnOx mixed oxides with different Ce/Mn ratios (0.25, 1 and 9). The obtained samples are characterized by wide-angle XRD, SAXS, N2 sorption, TPR-H2, TEM, UV–vis and Raman spectroscopies. The SBA-15 modification with CeMnOx decreases the sizes of NiO nanoparticles and enhances the NiO–support interaction. When Ce/Mn = 9, the NiO forms small particles on the surface of large CeO2 particles and/or interacts with CeO2, forming mixed phases. The best catalytic performance (at 650 °C, CH4 and CO2 conversions are 51 and 69%, respectively) is achieved over the Ni/CeMnOx/SBA-15 (9:1) catalyst. The peculiar CeMnOx composition (Ce/Mn = 9) also improves the catalyst stability: In a 24 h stability test, the CH4 conversion decreases by 18 rel.% as compared to a 30 rel.% decrease for unmodified catalyst. The enhanced catalytic stability of Ni/CeMnOx/SBA-15 (9:1) is attributed to the high concentration of reactive peroxo (O−) and superoxo (O2−) species that significantly lower the amount of coke in comparison with Ni-SBA-15 unmodified catalyst (weight loss of 2.7% vs. 42.2%). Ni-SBA-15 modified with equimolar Ce/Mn ratio or Mn excess is less performing. Ni/CeMnOx/SBA-15 (1:4) with the highest content of manganese shows the minimum conversions of reagents in the entire temperature range (X(CO2) = 4–36%, X(CH4) = 8–58%). This finding is possibly attributed to the presence of manganese oxide, which decorates the Ni particles due to its redistribution at the preparation stage.
Ni-Based SBA-15 Catalysts Modified with CeMnOx for CO2 Valorization via Dry Reforming of Methane: Effect of Composition on Modulating Activity and H2/CO Ratio
La Parola V.;Liotta L. F.
;
2023
Abstract
Dry reforming of methane with ratio CH4/CO2 = 1 is studied using supported Ni catalysts on SBA-15 modified by CeMnOx mixed oxides with different Ce/Mn ratios (0.25, 1 and 9). The obtained samples are characterized by wide-angle XRD, SAXS, N2 sorption, TPR-H2, TEM, UV–vis and Raman spectroscopies. The SBA-15 modification with CeMnOx decreases the sizes of NiO nanoparticles and enhances the NiO–support interaction. When Ce/Mn = 9, the NiO forms small particles on the surface of large CeO2 particles and/or interacts with CeO2, forming mixed phases. The best catalytic performance (at 650 °C, CH4 and CO2 conversions are 51 and 69%, respectively) is achieved over the Ni/CeMnOx/SBA-15 (9:1) catalyst. The peculiar CeMnOx composition (Ce/Mn = 9) also improves the catalyst stability: In a 24 h stability test, the CH4 conversion decreases by 18 rel.% as compared to a 30 rel.% decrease for unmodified catalyst. The enhanced catalytic stability of Ni/CeMnOx/SBA-15 (9:1) is attributed to the high concentration of reactive peroxo (O−) and superoxo (O2−) species that significantly lower the amount of coke in comparison with Ni-SBA-15 unmodified catalyst (weight loss of 2.7% vs. 42.2%). Ni-SBA-15 modified with equimolar Ce/Mn ratio or Mn excess is less performing. Ni/CeMnOx/SBA-15 (1:4) with the highest content of manganese shows the minimum conversions of reagents in the entire temperature range (X(CO2) = 4–36%, X(CH4) = 8–58%). This finding is possibly attributed to the presence of manganese oxide, which decorates the Ni particles due to its redistribution at the preparation stage.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.