HfB2-15 vol% MoSi2 composites were produced from powder mixtures and densified through different techniques, namely hot pressing and spark plasma sintering. Dense materials were obtained at 1900°C by hot pressing and at 1750°C by spark plasma sintering. Microstructure and mechanical properties were compared. The most relevant result was for high-temperature strength: independent of the processing technique, the flexural strength in air at 1500°C was higher than 500 MPa.
Fabrication and properties of HfB2-MoSi2 composites produced by hot pressing and spark plasma sintering
Diletta Sciti;Laura Silvestroni;Alida Bellosi
2006
Abstract
HfB2-15 vol% MoSi2 composites were produced from powder mixtures and densified through different techniques, namely hot pressing and spark plasma sintering. Dense materials were obtained at 1900°C by hot pressing and at 1750°C by spark plasma sintering. Microstructure and mechanical properties were compared. The most relevant result was for high-temperature strength: independent of the processing technique, the flexural strength in air at 1500°C was higher than 500 MPa.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.