Thermal residual stresses in SiC matrix MoSi2 reinforced composites were investigated by Raman microprobe spectroscopy. The introduction of 10 and 30 vol% MoSi2 particles generated compressive stresses in the SiC matrix, with magnitude of about -80 and -190 MPa, respectively. X-ray diffraction was also carried out and the agreement between the two techniques was quite satisfactory. From these results, the stress-free temperature of the composites was estimated.
Residual Stress Investigation in SiC/MoSi2(p) Composites
Diletta Sciti;Stefano Guicciardi;Giancarlo Celotti;
2007
Abstract
Thermal residual stresses in SiC matrix MoSi2 reinforced composites were investigated by Raman microprobe spectroscopy. The introduction of 10 and 30 vol% MoSi2 particles generated compressive stresses in the SiC matrix, with magnitude of about -80 and -190 MPa, respectively. X-ray diffraction was also carried out and the agreement between the two techniques was quite satisfactory. From these results, the stress-free temperature of the composites was estimated.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.