Holmium-doped BaTiO3 with composition Ba0.97Ho0.03TiO3 was prepared by sol-gel combustion method. A molar ratio of citrate/nitrate (CA/NO3=1.3) was used to prepare nanopowders of (Ba,Ho)TiO3. The structure and microstructure of (Ba,Ho)TiO3 powders and ceramics were investigated. The ceramics exhibit a dielectric constant of about 4400 and dielectric loss (tan d=0.267) at 10 Hz, and at the Curie temperature (Tc=132°C). The remanent polarization and the coercive field of Ba0.97Ho0.03TiO3 ceramics, at 1 kHz, were Pr=6 mC/cm2 and EC = 0.75 kV/cm. The dielectric and ferroelectric behavior of the holmium-doped BaTiO3 is influenced by the amphoteric character of Ho3+ ions
Electrical investigations of holmium-doped BaTiO3 derived from sol-gel combustion
Galassi C;
2010
Abstract
Holmium-doped BaTiO3 with composition Ba0.97Ho0.03TiO3 was prepared by sol-gel combustion method. A molar ratio of citrate/nitrate (CA/NO3=1.3) was used to prepare nanopowders of (Ba,Ho)TiO3. The structure and microstructure of (Ba,Ho)TiO3 powders and ceramics were investigated. The ceramics exhibit a dielectric constant of about 4400 and dielectric loss (tan d=0.267) at 10 Hz, and at the Curie temperature (Tc=132°C). The remanent polarization and the coercive field of Ba0.97Ho0.03TiO3 ceramics, at 1 kHz, were Pr=6 mC/cm2 and EC = 0.75 kV/cm. The dielectric and ferroelectric behavior of the holmium-doped BaTiO3 is influenced by the amphoteric character of Ho3+ ionsI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.