Influence of process changes on PCDD/Fs produced in an iron ore sintering plant

This study investigated the influence of different charge typologies and additives on the PCDD/Fs amount produced and on the congener profiles in an iron ore sintering plant. Many tests were carried out combining different typologies of charge (iron materials) and solid fuel ("coke breeze" or "anthracite") with or without the use of urea. The PCDD/Fs produced ranged from 1.2 to 22.7 g I-TEQ/ton of agglomerate, whereas the PCDD/Fs released to the ambient air ranged from 0.10 to 1.92 ng I-TEQ/Nm 3 because of cleaning in an elec-trostatic precipitator (ESP) and a Wetfine scrubber (WS). A more homogeneous charge with a higher amount of fine particles charge appeared to produce a lower PCDD/Fs concentration due to a better combustion but this hypothesis needs further investigations on charges having different dimension particles. Only a synergitic action of urea and anthracite was able to reduce the high PCDD/Fs content due to the bad combustion of the more inhomogeneous charge with a lower amount of fine particles. The congener profile was a typical com-bustion process fingerprint because the PCDFs predominated, the highly chlorinated congeners (HeptaCDD and OctaCDD) prevailed in PCDDs, whereas in PCDFs the profile was more varied; 1,2,3,4,6,7,8-HeptaCDF was the main contributor to the total concentration while 2,3,4,7,8-PentaCDF was the main contributor to the I-TEQ concentration. Whereas all the parameters under scrutiny influenced strongly the amount of PCDD/Fs produced, they affected only slightly the fingerprint of PCDD/Fs. In all cases studied, the reduction obtained using urea, anthracite, or the more homogeneous charge with a higher amount of fine particles was slightly greater on the higher chlorinated congeners in respect to the lower ones.