The equiatomic MoNbTaTiZr biocompatible and refractory high-entropy alloy (RHEA) was additively manufactured by laser powder bed fusion (LPBF). The possibility to reduce the cracking susceptibility of the RHEA during LPBF was investigated. By the addition of pure B to the RHEA powder feedstock, the in-situ precipitation of boride particles was promoted. These precipitates limited the grain growth, thus avoiding the formation of cracks.
Improvement of LPBF processability of equiatomic MoNbTaTiZr RHEA powder by in-situ precipitation of boride particles
Fiocchi J.;Biffi C. A.;
2024
Abstract
The equiatomic MoNbTaTiZr biocompatible and refractory high-entropy alloy (RHEA) was additively manufactured by laser powder bed fusion (LPBF). The possibility to reduce the cracking susceptibility of the RHEA during LPBF was investigated. By the addition of pure B to the RHEA powder feedstock, the in-situ precipitation of boride particles was promoted. These precipitates limited the grain growth, thus avoiding the formation of cracks.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
pre-proof.pdf
embargo fino al 28/06/2026
Tipologia:
Documento in Pre-print
Licenza:
Creative commons
Dimensione
2.79 MB
Formato
Adobe PDF
|
2.79 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.