Highlights High-entropy (Mn,Fe,Co,Ni,Zn) oxide nanofibers (NFs) are evaluated as LIB anodes. The existence of a microstructure-performance relationship is demonstrated. NFs with larger and less defective grains show superior stability and rate-capability. Best anodes deliver 453 mAh g−1 after 550 cycles at 0.5 A g−1, and 210 mAh g−1 at 2 A g−1. Long-term (≥650 cycles) capacity fading is due to the formation of Fe°, Co°, and Ni°.
Role of the Microstructure in the Li-Storage Performance of Spinel-Structured High-Entropy (Mn,Fe,Co,Ni,Zn) Oxide Nanofibers
Ponti A.;
2024
Abstract
Highlights High-entropy (Mn,Fe,Co,Ni,Zn) oxide nanofibers (NFs) are evaluated as LIB anodes. The existence of a microstructure-performance relationship is demonstrated. NFs with larger and less defective grains show superior stability and rate-capability. Best anodes deliver 453 mAh g−1 after 550 cycles at 0.5 A g−1, and 210 mAh g−1 at 2 A g−1. Long-term (≥650 cycles) capacity fading is due to the formation of Fe°, Co°, and Ni°.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
2024 - Role of the Microstructure in the Li-Storage Performance of Spinel-Structured High-Entropy (Mn,Fe,Co,Ni,Zn) Oxide Nanofibers.pdf
accesso aperto
Tipologia:
Versione Editoriale (PDF)
Licenza:
Creative commons
Dimensione
2.16 MB
Formato
Adobe PDF
|
2.16 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.