Preparation and characterization of hydroxyapatite coating by magnetron sputtering on Mg–Zn–Ag alloys for orthopaedic trauma implants

The aim of the present paper was to evaluate the effect of hydroxyapatite coatings on the two types of Mg–Zn–Ag alloys as a possible solution to control magnesium alloy degradation. The coatings were prepared by the radio frequency magnetron sputtering method at a deposition temperature of 300 °C. To perform this evaluation, the coated alloys were immersed in a simulated body fluid solution at body temperature (37 ± 0.5 °C) to determine the corrosion resistance through electrochemical and immersion tests. Moreover, the investigation also consisted of the evaluation of microchemical, mechanical, and morphological properties. The deposition temperature of 300 °C was enough to obtain a crystalline hydroxyapatite structure with a Ca/P ratio close to the stochiometric one. The adhesion of coatings was not influenced by the nature of Mg–Zn–Ag alloys, so similar values for both coated alloys were found. The results showed that the coating was homogonous deposited on the Mg–Zn–Ag alloys and the corrosion resistance of uncoated magnesium alloys was improved.