Yb:CaF2 transparent ceramics represent a promising laser gain medium for ultra-short lasers due to their characteristics: low phonon energy, relatively high thermal conductivity, negative thermo-optical coefficient, and low refractive index. Compared to single crystals, Yb:CaF2 ceramics offer superior mechanical properties, lower cost, and it is easier to obtain large-sized samples with proper shape and uniform Yb3+ doping at high concentrations. The combination of air pre-sintering and Hot Isostatic Pressing (HIP) emerges as a viable strategy for achieving high optical quality and fine-grained structure of ceramics at lower sintering temperatures. The properties of the powders used in ceramic fabrication critically influence both optical quality and laser performance of Yb:CaF2 ceramics. In this study, the 5 atomic percentage (at.%) Yb:CaF2 transparent ceramics were fabricated by air pre-sintering and hot isostatic pressing (HIP) using nano-powders synthesized through the co-precipitation method. The co-precipitated powders were optimized by studying air calcination temperature (from 350 to 550 °C). The influence of calcination temperature on the microstructure and laser performance of Yb:CaF2 ceramics was studied in detail. The 5 at.% Yb:CaF2 transparent ceramics air pre-sintered at 625 °C from powders air calcined at 400 °C and HIP post-treated at 600 °C exhibited the highest in-line transmittance of 91.5% at 1200 nm (3.0 mm thickness) and the best laser performance. Specifically, a maximum output power of 0.47 W with a maximum slope efficiency of 9.2% at 1029 nm under quasi-CW (QCW) pumping was measured.

Optimization of Yb:CaF2 Transparent Ceramics by Air Pre-Sintering and Hot Isostatic Pressing

Toci, Guido;Pirri, Angela;Patrizi, Barbara;Vannini, Matteo;
2024

Abstract

Yb:CaF2 transparent ceramics represent a promising laser gain medium for ultra-short lasers due to their characteristics: low phonon energy, relatively high thermal conductivity, negative thermo-optical coefficient, and low refractive index. Compared to single crystals, Yb:CaF2 ceramics offer superior mechanical properties, lower cost, and it is easier to obtain large-sized samples with proper shape and uniform Yb3+ doping at high concentrations. The combination of air pre-sintering and Hot Isostatic Pressing (HIP) emerges as a viable strategy for achieving high optical quality and fine-grained structure of ceramics at lower sintering temperatures. The properties of the powders used in ceramic fabrication critically influence both optical quality and laser performance of Yb:CaF2 ceramics. In this study, the 5 atomic percentage (at.%) Yb:CaF2 transparent ceramics were fabricated by air pre-sintering and hot isostatic pressing (HIP) using nano-powders synthesized through the co-precipitation method. The co-precipitated powders were optimized by studying air calcination temperature (from 350 to 550 °C). The influence of calcination temperature on the microstructure and laser performance of Yb:CaF2 ceramics was studied in detail. The 5 at.% Yb:CaF2 transparent ceramics air pre-sintered at 625 °C from powders air calcined at 400 °C and HIP post-treated at 600 °C exhibited the highest in-line transmittance of 91.5% at 1200 nm (3.0 mm thickness) and the best laser performance. Specifically, a maximum output power of 0.47 W with a maximum slope efficiency of 9.2% at 1029 nm under quasi-CW (QCW) pumping was measured.
2024
Istituto di Fisica Applicata - IFAC
Istituto Nazionale di Ottica - INO - Sede Secondaria di Sesto Fiorentino
air pre-sintering
hot isostatic pressing
laser performance
microstructure
Yb:CaF
2
transparent ceramics
File in questo prodotto:
File Dimensione Formato  
Li_Ceramics_Vol_ 7(3)_pp_1053_1065.pdf

accesso aperto

Tipologia: Versione Editoriale (PDF)
Licenza: Creative commons
Dimensione 9.46 MB
Formato Adobe PDF
9.46 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.14243/523507
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 3
  • ???jsp.display-item.citation.isi??? 1
social impact