Lattice Strain Relaxation and Compositional Control in As-Rich GaAsP/(100)GaAs Heterostructures Grown by MOVPE

The fabrication of high-efficiency GaAsP-based solar cells on GaAs wafers requires addressing structural issues arising from the materials lattice mismatch. We report on tensile strain relaxation and composition control of MOVPE-grown As-rich GaAs1-xPx/(100)GaAs heterostructures studied by double-crystal X-ray diffraction and field emission scanning electron microscopy. Thin (80-150 nm) GaAs1-xPx epilayers appear partially relaxed (within 1 12% of the initial misfit) through a network of misfit dislocations along the sample [011] and [01 (1) over bar] in plane directions. Values of the residual lattice strain as a function of epilayer thickness were compared with predictions from the equilibrium (Matthews-Blakeslee) and energy balance models. It is shown that the epilayers relax at a slower rate than expected based on the equilibrium model, an effect ascribed to the existence of an energy barrier to the nucleation of new dislocations. The study of GaAs1-xPx composition as a function of the V-group precursors ratio in the vapor during growth allowed for the determination of the As/P anion segregation coefficient. The latter agrees with values reported in the literature for P-rich alloys grown using the same precursor combination. P-incorporation into nearly pseudomorphic heterostructures turns out to be kinetically activated, with an activation energy E-A = 1.41 +/- 0.04 eV over the entire alloy compositional range.