A secondary ion mass spectrometry (SIMS) study of Zr- and Ti-based borides is reported: ZrB2 ceramic samples (with and without nickel addition) and a TiB2-Ni-B4C/Cu joint were investigated. For Zr-based samples, SIMS measurements show evidence for induced effects by the presence of nickel with regard to oxygen and hydrogen absorption and zirconia formation. In the case of the TiB2Ni-B4C/Cu joint, the ceramic-metal interface region was analysed and the extent of Cu diffusion into the ceramic material was established. SIMS results were in agreement with previously obtained SEM-EDS data.
Secondary ion mass spectrometry in the characterisation of boron-based ceramics
Daolio S;Fabrizio M;Piccirillo C;Muolo ML;Passerone A;Bellosi A
2001
Abstract
A secondary ion mass spectrometry (SIMS) study of Zr- and Ti-based borides is reported: ZrB2 ceramic samples (with and without nickel addition) and a TiB2-Ni-B4C/Cu joint were investigated. For Zr-based samples, SIMS measurements show evidence for induced effects by the presence of nickel with regard to oxygen and hydrogen absorption and zirconia formation. In the case of the TiB2Ni-B4C/Cu joint, the ceramic-metal interface region was analysed and the extent of Cu diffusion into the ceramic material was established. SIMS results were in agreement with previously obtained SEM-EDS data.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.