One-Pot Sr-Free LaFeO3/CeO2-Based Electrocatalytic Composites: Effect of Cerium and Lanthanum Interplay Between Perovskite and Fluorite

Perovskite-type oxides are among the most promising cathodes for intermediate-temperature solid oxide fuel cells (IT-SOFCs) due to their mixed ionic–electronic conductivity and compositional flexibility. Many high-performance cathodes rely on Sr substitution at the A-site, often associated with surface segregation and long-term degradation. In this work, we explore an alternative strategy based on defect engineering and phase interactions in Sr-free composites. Perovskite-fluorite composites based on LaFe0.8Co0.2O3 were synthesized through a one-pot route designed to promote the formation of a perovskite phase and a limited amount of fluorite-type ceria. This approach allows the introduction of small fractions of Ce into the perovskite lattice, favoring the cooperative coexistence with La-doped CeO2. Structural, microstructural and spectroscopic characterization indicates that Ce influences the crystallization pathway and composite defect chemistry. Variations in lattice parameters and Raman features suggest modifications of perovskite structure consistent with defect formation and lattice distortion. Reduction properties and electrical conductivity measurements indicate that Ce incorporation in the perovskite and oxide interaction affect charge transport and oxygen mobility. The electrochemical results demonstrate that the optimal trade-off between activation energy (Ea) and polarization resistance (Rp) is achieved for the sample, with a nominal cerium content, Ce/(La + Ce) of 0.16. Moreover, the electrochemical properties are found to correlate with the nominal cerium content, which regulates defect chemistry and the resulting composite composition. Overall, results suggest that the one-pot synthesis promotes beneficial interactions between the perovskite and ceria phases, allowing the development of Sr-free ferrite-based materials with enhanced functional properties, minimizing the amount of ceria in the composite.