Iron oxide doped silica films and powders with highly ordered mesostructures of extraordinary temperature stability (up to 1000 degrees C) and iron loading of up to 6 atom% were produced by the use of novel iron alkoxide-coordinated surfactants. Wormhole-like, 2d-centered rectangular, orthorhombic and lamellar mesostructures were obtained by variation of the molar ratios of the metal-surfactant complexes. The influence of a subsequent heat treatment was studied by GI-SAXS, TEM, XRD, and nitrogen sorption techniques. The molecular composition of the films was studied by XPS and EXAFS.
Synthesis and characterization of orthorhombic, 2d-centered rectangular and lamellar iron oxide doped silica films
Gross S
2006
Abstract
Iron oxide doped silica films and powders with highly ordered mesostructures of extraordinary temperature stability (up to 1000 degrees C) and iron loading of up to 6 atom% were produced by the use of novel iron alkoxide-coordinated surfactants. Wormhole-like, 2d-centered rectangular, orthorhombic and lamellar mesostructures were obtained by variation of the molar ratios of the metal-surfactant complexes. The influence of a subsequent heat treatment was studied by GI-SAXS, TEM, XRD, and nitrogen sorption techniques. The molecular composition of the films was studied by XPS and EXAFS.File in questo prodotto:
| File | Dimensione | Formato | |
|---|---|---|---|
|
prod_47782-doc_53918.pdf
solo utenti autorizzati
Descrizione: Synthesis and characterization of orthorhombic, 2d-centered rectangular and lamellar iron oxide doped silica films
Dimensione
917.03 kB
Formato
Adobe PDF
|
917.03 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.