A composite Nafion-TiO2 membrane was manufactured by a recast procedure, using an in-house prepared TiO2. This membrane has shown promising properties for high temperature operation in an SPE electrolyser allowing to achieve higher performance with respect to a commercial Nafion 115 membrane. This effect is mainly due to the water retention properties of the TiO2 filler. A promising increase in electrical efficiency was recorded at low current densities for the composite membrane-based SPE electrolyser at high temperature compared to conventional membrane-based devices.
Solid polymer electrolyte water electrolyser based on nafion-TiO2 composite membrane for high temperature operation
Baglio V;Ciccarella G;Antonucci V;
2009
Abstract
A composite Nafion-TiO2 membrane was manufactured by a recast procedure, using an in-house prepared TiO2. This membrane has shown promising properties for high temperature operation in an SPE electrolyser allowing to achieve higher performance with respect to a commercial Nafion 115 membrane. This effect is mainly due to the water retention properties of the TiO2 filler. A promising increase in electrical efficiency was recorded at low current densities for the composite membrane-based SPE electrolyser at high temperature compared to conventional membrane-based devices.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.