The challenge to develop high piezoelectric sensitivity and lead-free composition ferro-piezoelectric ce-ramics has recently dragged new attention to some classic ferroelectrics. Here, Ba(CexTi1-x)O3 (Ce-BT) and 0.94(Bi1/2Na1/2 )TiO3-0.06BaTiO3(BNBT6) ceramics were piezoelectrically characterized from measurements of complex impedance at electromechanical resonances and their analysis by Alemany et al. software. The reconstruction of the spectra for each resonance is used as an accuracy test of the set of calculated coef- ficients, quantitatively characterized by the regression factor (R2) of such reconstruction to the experimental spectrum. Piezoelectric activity at room temperature (RT) was observed for Ce-BT with x=0.06 and 0.1, ferroelectrics with T(ε´max)RT, but also for x=0.2 with T(ε´max)RT, which confirms its relaxor character (Ps≠0 for T≥T(ε´max)). BNBT6 fine grained ceramics (~1 μm) were prepared from nanopowder obtained by sol-gel autocombustion. Results obtained for the fine grained ceramic hot-pressed at 800ºC for 2 h and recrystallized at 1050°C for 1h are d331100°C. Some measurement issues, as the role of the mode coupling on the characterization results, illustrated for the shear mode of a thickness poled plate, are discussed
Piezoelectric characterization of lead-free ferroelectric ceramics
Mercadelli E;Galassi C
2010
Abstract
The challenge to develop high piezoelectric sensitivity and lead-free composition ferro-piezoelectric ce-ramics has recently dragged new attention to some classic ferroelectrics. Here, Ba(CexTi1-x)O3 (Ce-BT) and 0.94(Bi1/2Na1/2 )TiO3-0.06BaTiO3(BNBT6) ceramics were piezoelectrically characterized from measurements of complex impedance at electromechanical resonances and their analysis by Alemany et al. software. The reconstruction of the spectra for each resonance is used as an accuracy test of the set of calculated coef- ficients, quantitatively characterized by the regression factor (R2) of such reconstruction to the experimental spectrum. Piezoelectric activity at room temperature (RT) was observed for Ce-BT with x=0.06 and 0.1, ferroelectrics with T(ε´max)RT, but also for x=0.2 with T(ε´max)RT, which confirms its relaxor character (Ps≠0 for T≥T(ε´max)). BNBT6 fine grained ceramics (~1 μm) were prepared from nanopowder obtained by sol-gel autocombustion. Results obtained for the fine grained ceramic hot-pressed at 800ºC for 2 h and recrystallized at 1050°C for 1h are d331100°C. Some measurement issues, as the role of the mode coupling on the characterization results, illustrated for the shear mode of a thickness poled plate, are discussedI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.