Solid state reaction method was used to prepare high-Tc phases of (Bi0.7Pb0.3)2 AgxSr2Ca2Cu3O10+δ (0 ≤ x ≤ 0.5) superconductors. The samples were studied to investigate the effect of Ag addition on the superconducting properties. The phase composition and the microstructure were analyzed by XRD and SEM/EDX, while the physical properties were determined by means of transport and magnetic measurements. The experimental data indicate that the Ag content infl uences the relative amount of competing phase (namely Bi-2223 and Bi-2212).
Superconductivity of (Bi0.7Pb0.3)2AgxSr2Ca2Cu3O10+?δ(0≤x≤ 0.5)
Gilioli E
2009
Abstract
Solid state reaction method was used to prepare high-Tc phases of (Bi0.7Pb0.3)2 AgxSr2Ca2Cu3O10+δ (0 ≤ x ≤ 0.5) superconductors. The samples were studied to investigate the effect of Ag addition on the superconducting properties. The phase composition and the microstructure were analyzed by XRD and SEM/EDX, while the physical properties were determined by means of transport and magnetic measurements. The experimental data indicate that the Ag content infl uences the relative amount of competing phase (namely Bi-2223 and Bi-2212).File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.