The morphological analysis of a commercial polycarbonate based waterborne polyurethane was carried out by transmission electron microscopy. The polyurethane, after purification, exhibits a nanostructured phase separation between hard and soft domains. Thermal analysis showed two Tgs corresponding to the hard and soft domains respectively.
L'osservazione al microscopio elettronico a trasmissione (TEM) ha permesso di studiare la morfologia di un poliuretano commerciale a base policarbonato in dispersione acquosa. Dopo purificazione, è stata evidenziata la nanoseparazione di fase tra i domini hard e soft, confermata anche dall'analisi termica che mostra per essi due Tg distinte.
Poliuretani lineari: osservazione TEM della loro nanostruttura
Dondero G;Conzatti L;Stagnaro P;
2009
Abstract
The morphological analysis of a commercial polycarbonate based waterborne polyurethane was carried out by transmission electron microscopy. The polyurethane, after purification, exhibits a nanostructured phase separation between hard and soft domains. Thermal analysis showed two Tgs corresponding to the hard and soft domains respectively.File | Dimensione | Formato | |
---|---|---|---|
prod_72113-doc_42429.pdf
solo utenti autorizzati
Descrizione: articolo pubblicato
Dimensione
540.67 kB
Formato
Adobe PDF
|
540.67 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.