The high temperature reaction between the superconducting Nd123(x) (Nd1+xBa2-xCu3O7-?+x/2) phase and Nd422(z) (Nd4-2zBa2+2zCu2-zO10-2z), leading to substitutions of Nd in the Ba sites of Nd123, was analysed. For this purpose, differential thermal analysis (DTA) was performed on powders with different Nd422 addition. Measurement results were compared with the values, reported in the literature, of the peritectic temperatures in function of Nd123 substitution. The superconducting transition critical temperature analysis of melt-textured samples shows that the use of Barium rich Nd422 allows significant improvements of the superconducting parameters of produced samples, avoiding the occurrence of the Nd-Ba substitutions.
Reactivity Between Nd1+xBa2-xCu3O7-?+x/2 and Nd4-2zBa2+2zCu2-zO10-2z Phases in Superconducting NdBaCuO Powders and Melt Textured Bulk Samples
Marcello Gombos;Antonio Vecchione;Sandro Pace;
2003
Abstract
The high temperature reaction between the superconducting Nd123(x) (Nd1+xBa2-xCu3O7-?+x/2) phase and Nd422(z) (Nd4-2zBa2+2zCu2-zO10-2z), leading to substitutions of Nd in the Ba sites of Nd123, was analysed. For this purpose, differential thermal analysis (DTA) was performed on powders with different Nd422 addition. Measurement results were compared with the values, reported in the literature, of the peritectic temperatures in function of Nd123 substitution. The superconducting transition critical temperature analysis of melt-textured samples shows that the use of Barium rich Nd422 allows significant improvements of the superconducting parameters of produced samples, avoiding the occurrence of the Nd-Ba substitutions.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.