Hydrogenated silicon-carbon thin films were deposited by Radio Frequency Plasma Enhanced Chemical Vapor Deposition using silane-methane gas mixtures highly diluted in hydrogen. The effects of the presence of a microcrystalline silicon seed layer and of the methane flow rate during deposition were investigated in order to find the optimal conditions for microcrystalline growth. The presence of a seed layer promotes the amorphous to microcrystalline transition at the interface with the substrate, reducing the incubation layer to a 5-10 nm thickness. At the same time, an excessive increase in the CH4 flow rate suppresses crystalline growth, leading to extremely flat amorphous samples (root-mean-square surface roughness rho(RMS) similar to 0.5 nm), even with a seed layer. The total carbon content was measured by Radio Frequency Glow Discharge Optical Emission Spectroscopy. It was found that carbon is only incorporated in the amorphous tissue, and not in the crystalline phase. Thus, the increase of the crystalline fraction, directly linked to the increase of the seed layer deposition time, leads to a decrease of the carbon incorporation in the subsequent layer. (C) 2013 Elsevier B.V. All rights reserved.
Structural properties of hydrogenated microcrystalline silicon-carbon alloys deposited by Radio Frequency Plasma Enhanced Chemical Vapor Deposition: Effect of microcrystalline silicon seed layer and methane flow rate
Ruggeri R;Mannino G;
2014
Abstract
Hydrogenated silicon-carbon thin films were deposited by Radio Frequency Plasma Enhanced Chemical Vapor Deposition using silane-methane gas mixtures highly diluted in hydrogen. The effects of the presence of a microcrystalline silicon seed layer and of the methane flow rate during deposition were investigated in order to find the optimal conditions for microcrystalline growth. The presence of a seed layer promotes the amorphous to microcrystalline transition at the interface with the substrate, reducing the incubation layer to a 5-10 nm thickness. At the same time, an excessive increase in the CH4 flow rate suppresses crystalline growth, leading to extremely flat amorphous samples (root-mean-square surface roughness rho(RMS) similar to 0.5 nm), even with a seed layer. The total carbon content was measured by Radio Frequency Glow Discharge Optical Emission Spectroscopy. It was found that carbon is only incorporated in the amorphous tissue, and not in the crystalline phase. Thus, the increase of the crystalline fraction, directly linked to the increase of the seed layer deposition time, leads to a decrease of the carbon incorporation in the subsequent layer. (C) 2013 Elsevier B.V. All rights reserved.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.