We synthesized ultrathin Si nanowires (NWs) by metal assisted chemical wet etching, using a very thin discontinuous Au layer as precursor for the process. A bright room temperature emission in the visible range due to electron-hole recombination in quantum confined Si NWs is reported. A single walled carbon nanotube (CNT) suspension was prepared and dispersed in Si NW samples. The hybrid Si NW/CNT system exhibits a double emission at room temperature, both in the visible (due to Si NWs) and the IR (due to CNTs) range, thus demonstrating the realization of a low-cost material with promising perspectives for applications in Si-based photonics.
A room temperature light source based on silicon nanowires
Lo Faro M J;D'Andrea C;Messina E;Fazio B;Franzò G;Gucciardi P G;Vasi C;Priolo F;Iacona F;Irrera A
2016
Abstract
We synthesized ultrathin Si nanowires (NWs) by metal assisted chemical wet etching, using a very thin discontinuous Au layer as precursor for the process. A bright room temperature emission in the visible range due to electron-hole recombination in quantum confined Si NWs is reported. A single walled carbon nanotube (CNT) suspension was prepared and dispersed in Si NW samples. The hybrid Si NW/CNT system exhibits a double emission at room temperature, both in the visible (due to Si NWs) and the IR (due to CNTs) range, thus demonstrating the realization of a low-cost material with promising perspectives for applications in Si-based photonics.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.