Nanostructured thin films are widely investigated for application in multifunctional devices thanks to their peculiar optoelectronic properties. In this work anatase TiO nanoparticles (average diameter 10 nm) synthesised by a green aqueous sol-gel route are exploited to fabricate optically active electrodes for pseudocapacitive-electrochromic devices. In our approach, highly transparent and homogeneous thin films having a good electronic coupling between nanoparticles are prepared. These electrodes present a spongy-like nanostructure in which the dimension of native nanoparticles is preserved, resulting in a huge surface area. Cyclic voltammetry studies reveal that there are significant contributions to the total stored charge from both intercalation capacitance and pseudocapacitance, with a remarkable 50% of the total charge deriving from this second effect. Fast and reversible colouration occurs, with an optical modulation of ~60% in the range of 315-1660 nm, and a colouration efficiency of 25.1 cm C at 550 nm. This combination of pseudocapacitance and electrochromism makes the sol-gel derived titania thin films promising candidates for multifunctional 'smart windows'.
Pseudocapacitive behaviour in sol-gel derived electrochromic titania nanostructures
Giannuzzi Roberto;Tobaldi David M;Pugliese Marco;de Marco Luisa;Carallo Sonia;Gigli Giuseppe;Maiorano Vincenzo
2021
Abstract
Nanostructured thin films are widely investigated for application in multifunctional devices thanks to their peculiar optoelectronic properties. In this work anatase TiO nanoparticles (average diameter 10 nm) synthesised by a green aqueous sol-gel route are exploited to fabricate optically active electrodes for pseudocapacitive-electrochromic devices. In our approach, highly transparent and homogeneous thin films having a good electronic coupling between nanoparticles are prepared. These electrodes present a spongy-like nanostructure in which the dimension of native nanoparticles is preserved, resulting in a huge surface area. Cyclic voltammetry studies reveal that there are significant contributions to the total stored charge from both intercalation capacitance and pseudocapacitance, with a remarkable 50% of the total charge deriving from this second effect. Fast and reversible colouration occurs, with an optical modulation of ~60% in the range of 315-1660 nm, and a colouration efficiency of 25.1 cm C at 550 nm. This combination of pseudocapacitance and electrochromism makes the sol-gel derived titania thin films promising candidates for multifunctional 'smart windows'.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.