In this work, dewetting process has been investigated in shape-memory Heuslers. To this aim, series of high-temperature annealing (1100-1150 K) have been performed at high vacuum (time is varied in the range of 55-165 min) in Ni-Mn-Ga epitaxial thin films grown on MgO(001). The process kinetics have been followed by studying the evolution of morphology and composition. In particular, we report the initiation of the dewetting process by the formation of symmetric holes in the films. The holes propagate and integrate, leaving micrometric and submicron islands of the material, increasing the average roughness of the films by a factor of up to around 30. The dewetting process is accompanied by severe Ga and Mn sublimation, and Ni-Ga segregation, which significantly modify the magnetic properties of the films measured at each stage. The annealed samples show a relatively weak magnetic signal at room temperature with respect to the pristine sample
Dewetting Process in Ni-Mn-Ga Shape-Memory Heusler: Effects on Morphology, Stoichiometry and Magnetic Properties
Takhsha Ghahfarokhi M;Casoli F;Albertini F
2022
Abstract
In this work, dewetting process has been investigated in shape-memory Heuslers. To this aim, series of high-temperature annealing (1100-1150 K) have been performed at high vacuum (time is varied in the range of 55-165 min) in Ni-Mn-Ga epitaxial thin films grown on MgO(001). The process kinetics have been followed by studying the evolution of morphology and composition. In particular, we report the initiation of the dewetting process by the formation of symmetric holes in the films. The holes propagate and integrate, leaving micrometric and submicron islands of the material, increasing the average roughness of the films by a factor of up to around 30. The dewetting process is accompanied by severe Ga and Mn sublimation, and Ni-Ga segregation, which significantly modify the magnetic properties of the films measured at each stage. The annealed samples show a relatively weak magnetic signal at room temperature with respect to the pristine sampleFile | Dimensione | Formato | |
---|---|---|---|
Dewetting Process in Ni-Mn-Ga Shape-Memory Heusler: Effects on Morphology, Stoichiometry and Magnetic Properties.pdf
accesso aperto
Descrizione: A
Tipologia:
Versione Editoriale (PDF)
Licenza:
Creative commons
Dimensione
8.37 MB
Formato
Adobe PDF
|
8.37 MB | Adobe PDF | Visualizza/Apri |
crystals-2051937-supplementary.pdf
accesso aperto
Descrizione: Supplementary Materials
Tipologia:
Versione Editoriale (PDF)
Licenza:
Creative commons
Dimensione
745.16 kB
Formato
Adobe PDF
|
745.16 kB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.