Nanoscale Chemical Analysis of Thin Film Solar Cell Interfaces Using Tip-Enhanced Raman Spectroscopy

Interfacial regions play a key role in determining the overall power conversion efficiency of thin film solar cells. However, the nanoscale investigation of thin film interfaces using conventional analytical tools is challenging due to a lack of required sensitivity and spatial resolution. Here, we surmount these obstacles using tip-enhanced Raman spectroscopy (TERS) and apply it to investigate the absorber (Sb2Se3) and buffer (CdS) layers interface in a Sb2Se3-based thin film solar cell. Hyperspectral TERS imaging with 10 nm spatial resolution reveals that the investigated interface between the absorber and buffer layers is far from uniform, as TERS analysis detects an intermixing of chemical compounds instead of a sharp demarcation between the CdS and Sb2Se3 layers. Intriguingly, this interface, comprising both Sb2Se3 and CdS compounds, exhibits an unexpectedly large thickness of 295 ± 70 nm attributable to the roughness of the Sb2Se3 layer. Furthermore, TERS measurements provide compelling evidence of CdS penetration into the Sb2Se3 layer, likely resulting from unwanted reactions on the absorber surface during chemical bath deposition. Notably, the coexistence of ZnO, which serves as the uppermost conducting layer, and CdS within the Sb2Se3-rich region has been experimentally confirmed for the first time. This study underscores TERS as a promising nanoscale technique to investigate thin film inorganic solar cell interfaces, offering novel insights into intricate interface structures and compound intermixing.