Compositionally complex AlB2-type diborides in dissociated air plasma

Multi-metal compositionally complex (CC) AlB2-type diboride solid solutions (SS) containing IV-V-VI group elements are garnering a steadily growing research interest. The present work explores the composition dependence of oxidation resistance on nominally equiatomic (Hf,Me,Ta,Ti,Zr)B2 SS, Me = Nb or Cr, exposed to a dissociated air plasma (total pressure of about 1 kPa): specimens were exposed for 5 min at some selected set points between 1800 K and 2500 K using a solar furnace. The CC diboride with Nb showed superior resistance to oxidation compared to that with Cr. The experimental results showed good agreement with predictions based on a thermodynamic assessment