: This work provides a comprehensive investigation of nitrogen and aluminum doping and its consequences for the physical properties of 3C-SiC. Free-standing 3C-SiC heteroepitaxial layers, intentionally doped with nitrogen or aluminum, were grown on Si (100) substrate with different 4° off-axis in a horizontal hot-wall chemical vapor deposition (CVD) reactor. The Si substrate was melted inside the CVD chamber, followed by the growth process. Micro-Raman, photoluminescence (PL) and stacking fault evaluation through molten KOH etching were performed on different doped samples. Then, the role of the doping and of the cut angle on the quality, density and length distribution of the stacking faults was studied, in order to estimate the influence of N and Al incorporation on the morphological and optical properties of the material. In particular, for both types of doping, it was observed that as the dopant concentration increased, the average length of the stacking faults (SFs) increased and their density decreased.

Effect of nitrogen and aluminum doping on 3c-sic heteroepitaxial layers grown on 4◦ off-axis si (100)

Calabretta C.;Scuderi V.
;
Cannizzaro A.;Boninelli S.;La Via F.
2021

Abstract

: This work provides a comprehensive investigation of nitrogen and aluminum doping and its consequences for the physical properties of 3C-SiC. Free-standing 3C-SiC heteroepitaxial layers, intentionally doped with nitrogen or aluminum, were grown on Si (100) substrate with different 4° off-axis in a horizontal hot-wall chemical vapor deposition (CVD) reactor. The Si substrate was melted inside the CVD chamber, followed by the growth process. Micro-Raman, photoluminescence (PL) and stacking fault evaluation through molten KOH etching were performed on different doped samples. Then, the role of the doping and of the cut angle on the quality, density and length distribution of the stacking faults was studied, in order to estimate the influence of N and Al incorporation on the morphological and optical properties of the material. In particular, for both types of doping, it was observed that as the dopant concentration increased, the average length of the stacking faults (SFs) increased and their density decreased.
2021
Istituto per la Microelettronica e Microsistemi - IMM
3C-SiC
KOH etching
doping
stacking faults
File in questo prodotto:
File Dimensione Formato  
Materials 2021, 14, 4400.pdf

accesso aperto

Tipologia: Versione Editoriale (PDF)
Licenza: Creative commons
Dimensione 3.66 MB
Formato Adobe PDF
3.66 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.14243/514278
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? ND
social impact